Commercial Pure Titanium Grade 2 Bar and Rod

1.Titanium Alloy Grade 2 is “unalloyed” titanium offering an excellent balance of strength and ductility.
2.The material has good toughness and is readily weldable. This material is very corrosion resistant in highly oxidizing and mildly reducing environments.
3.Size: Φ7mm~Φ230mm;

Products Inquiry

CompanyName * :

Email * :

Name :

Tel :

Message :

Product Details

Titanium Alloy Grade 2 is “unalloyed” titanium offering an excellent balance

of strength and ductility. The material has good toughness and is readily

weldable. This material is very corrosion resistant in highly oxidizing and

mildly reducing environments.

Standard Specification: ASTM B348, ASME SB348, ASTM F67 Surgical Implant, ISO, DIN AMS-T-9046B CP3 AMS 4902 MIL-T-9046J CP

Standard	Werkstoff No.	UNS
Commercial Pure Titanium Grade2	3.7035	R50400

Technical Data Sheet

Chemical Composition
Weight %	Ti	C	Fe	N	O	H
Commercial Pure Titanium Grade2	Balance	0.08	0.3	0.03	0.25	0.015

Typical Mechanical Properties (Tensile Requirements)

Material

Tensile Strength, min

Yield Strength (0.2% Offset) min or range

Elongation in 4D,min%

Reduction of Area

Min %

ksi

MPa

ksi

MPa

Commercial Pure Titanium Grade2

345

275

Titanium Alloy Grade 36 Ti45-Nb Bar and Rod

Standard Specification: ASTM B348, ASME SB348, ISO, DINAWS A5.16 (ERTi-36); Standard Werkstoff No. UNS Titanium Al

AMS Titanium Alloy Grade 6 (Ti-5Al-2.5Sn) Bar and Rod

Titanium Ti5Al2.5Sn (Grade 6) is a high strength alloy which is most commonly used in airframe and jet engine applications. Titanium Ti5Al2.5Sn (Grade 6) has good weldability, stability and strength

AMS Titanium Alloy 8-1-1 ( 8Al-1Mo-1V) Bar and Rod

Titanium 8-1-1 (8Al-1Mo-1V) is a near alpha alloy offering good weldability and with superior creep resistance at operating temperature up to 450°C. Alloy 8-1-1 has a relatively high tensile modulus

Titanium Alloy Grade 12 Ti-0.3Mo-0.8Ni Bar and Rod